Patent application number | Description | Published |
20140000765 | COLD-ROLLED STEEL SHEET AND PRODUCTION METHOD THEREOF | 01-02-2014 |
20140014236 | HOT-ROLLED STEEL SHEET AND PRODUCTION METHOD THEREOF - Disclosed is a hot-rolled steel sheet including, by mass %, C:0.02% to 0.5% of C, and the sum of the content of Si and the content of Al is 1.0% to 4.0%. An average pole density of an orientation group from {100}<011> to {223}<110> is 1.0 to 6.5, and a pole density of a crystal orientation {332}<113> is 1.0 to 5.0. A microstructure includes, by of an area ratio, 2% to 30% of retained austenite, 20% to 50% of ferrite, and 10% to 60% of bainite. rC that is a Lankford value in a direction orthogonal to a rolling direction is 0.70 to 1.10, and r30 that is a Lankford value in a direction forming an angle of 30° with the rolling direction is 0.70 to 1.10. | 01-16-2014 |
20140045252 | CELL CULTIVATION CONTAINER AND CELL CULTURING APPARATUS - Provided is a cell cultivation container equipped with electrodes, which enables automatic culturing, observation of automatically cultured cells, and measurement of electrical resistances. A circular electrode ( | 02-13-2014 |
20140087455 | Cell Culture Device and Transport Device - The present invention provides a carrier device including a culture vessel and a flow channel, which have a closed structure, for supplying cell liquid or a culture medium into the flow channel; and a method of aseptically injecting liquid, such as the cell or the culture medium, into the culture vessel and the flow channel. The present invention provides a carrier jig | 03-27-2014 |
20140234657 | HOT-DIP GALVANIZED STEEL SHEET AND MANUFACTURING METHOD THEREOF - A hot-dip galvanized steel sheet includes: a steel sheet; and a plated layer on a surface of the steel sheet, a microstructure contains, by volume fraction, equal to or more than 20% and equal to or less than 99% in total of one or two of martensite and bainite, a residual structure contains one or two of ferrite, residual austenite of less than 8% by volume fraction, and pearlite of equal to or less than 10% by volume fraction, tensile strength is equal to or greater than 980 MPa, the plated layer is a hot-dip galvanized layer which contains oxides including one or two or more of Si, Mn, and Al, contains equal to or less than 15 mass % of Fe, and a remainder including Zn, Al, and unavoidable impurities, and when a cross section including the steel sheet and the hot-dip galvanized layer is seen in a sheet thickness direction, a projected area ratio is equal to or more than 10% and equal to or less than 90%. | 08-21-2014 |
20140234658 | GALVANIZED STEEL SHEET AND METHOD OF MANUFACTURING THE SAME - A galvanized steel sheet includes a steel sheet and a plating layer on the surface of the steel sheet, in which the steel sheet includes, as a steel chemical composition, by mass %, C: 0.05 to 0.40%, Si: 0.5 to 3.0% and Mn: 1.5 to 3.0%, a microstructure of the steel sheet includes ferrite, bainite, by volume fraction, 30% or more of a tempered martensite, and 8% or more of an austenite, and tensile strength of the steel sheet is 980 MPa or more, and the plating layer includes an oxide including at least one chemical element selected from Si, Mn and Al, and when seen at a cross section including the steel sheet and the plating layer in a plate thickness direction, a projection area fraction of the oxide is 10% or more. | 08-21-2014 |
20140242415 | HIGH-STRENGTH HOT-DIP GALVANIZED STEEL SHEET AND HIGH-STRENGTH ALLOYED HOT-DIP GALVANIZED STEEL SHEET HAVING EXCELLENT FORMABILITY AND SMALL MATERIAL ANISOTROPY WITH ULTIMATE TENSILE STRENGTH OF 980 MPa OR MORE AND MANUFACTURING METHOD THEREFOR - Provided is a high-strength hot-dip galvanized steel sheet having small material anisotropy and excellent formability with an ultimate tensile strength of 980 MPa or more. The hot-dip galvanized steel sheet includes a hot-dip galvanized layer formed on a surface of a base steel plate. The base steel plate contains, by mass %, C: 0.1 to less than 0.40%, Si: 0.5 to 3.0%, Mn: 1.5 to 3.0%, O: limited to 0.006% or less, P: limited to 0.04% or less, S: limited to 0.01% or less, Al: limited to 2.0% or less, N: limited to 0.01% or less, and a balance including Fe and inevitable impurities. A microstructure of the base steel sheet contains ferrite of 40% or more, residual austenite of 8 to less than 60%, by volume fraction, and a balance being bainite or martensite. In a sheet thickness range of ⅝ to ⅜ from the surface of the base steel sheet, a pole density of specific crystal orientation is within a predetermined range. The hot-dip galvanized layer contains Fe: less than 7 mass % and a balance including Zn, Al, and inevitable impurities. | 08-28-2014 |
20140377582 | HIGH-STRENGTH COLD-ROLLED STEEL SHEET AND METHOD FOR PRODUCING THE SAME - A high-strength cold-rolled steel sheet includes, as a component composition, by mass %: C: 0.075% to 0.300%; Si: 0.30% to 2.50%; Mn: 1.30% to 3.50%; P: 0.001% to 0.050%; S: 0.0001% to 0.0100%; Al: 0.001% to 1.500%; and N: 0.0001% to 0.0100%, in which a surface microstructure contains residual austenite of 3% to 10% and ferrite of 90% or less by volume fraction, an inner microstructure at a depth of t/4 from the surface assuming that a sheet thickness is t contains residual austenite of 3% to 20% by volume fraction, a ratio Hvs/Hvb between a surface hardness Hvs of the steel sheet surface and a hardness Hvb at a depth of ¼ of the thickness is more than 0.75 to 0.90, and a maximum tensile strength is 700 MPa or more. | 12-25-2014 |
20150072401 | CULTURE VESSEL AND AUTOMATED CULTURE APPARATUS - In a closed system culture vessel to be used in an automated culture apparatus, some of the ports perform both liquid supply and gas supply functions. Culture medium is thereby made to flow always in one direction. The culture vessel is also configured so that, in the complete culture medium exchange process and the effluent recovery process for analyzing culture medium components, waste liquid medium does not get mixed into fresh culture medium. | 03-12-2015 |