20100022679 | USE OF TIMBER MATERIALS COMPRISING POLYAMINE FOR LOWERING FORMALDEHYDE CONTENT IN AMBIENT AIR - The present invention relates to the use of wood-base materials for the production of furniture parts, wall claddings, insulation materials and the like for reducing the formaldehyde content in the ambient air, the wood-base materials
| 01-28-2010 |
20100190021 | METHOD FOR REDUCTION OF FORMALDEHYDE EMISSIONS IN WOOD MATERIALS - The present invention relates to a method for the reduction of the formaldehyde emission of wood-base materials by application of nitrogen-containing compounds, wherein
| 07-29-2010 |
20100297425 | LIGHT WOOD-BASED MATERIALS - The present invention relates to light wood-base materials comprising from 30 to 92.5% by weight, based on the wood-base material, of wood particles, the wood particles having a mean density of from 0.4 to 0.85 g/cm | 11-25-2010 |
20110003136 | LIGHT WOOD-BASED MATERIALS - A light wood-containing material having an average density in the range from 200 to 600 kg/m | 01-06-2011 |
20110008608 | COMPOSITE MOLDING IN PARTICULAR FOR FURNITURE CONSTRUCTION - A composite molding, in particular for furniture construction, comprises a core layer and one or more further layers, where the core layer takes the form of a molded-foam molding, obtainable via fusion of prefoamed foam beads composed of expandable, thermoplastic polymer pellets comprising
| 01-13-2011 |
20110039090 | LIGHT WOOD-BASED MATERIALS HAVING GOOD MECHANICAL PROPERTIES AND LOW FORMALDEHYDE EMISSION - A light wood-containing material having an average density in the range from 200 to 600 kg/m | 02-17-2011 |
20110130080 | FLEXIBLE, FLAT SUBSTRATE WITH AN ABRASIVE SURFACE - Flexible, sheet-like substrates having an abrasive surface, which are obtainable by applying an aqueous solution or dispersion of at least one precondensate of a heat-curable resin to the top and/or bottom of a flexible, sheet-like substrate in an amount in the range from 0.1 to 90% by weight, based on the uncoated, dry substrate, crosslinking the precondensate and drying the treated substrate, wherein the aqueous solution or dispersion of at least one precondensate of a heat-curable resin comprises (i) a polymeric thickener selected from the group consisting of biopolymers, associative thickeners and wholly synthetic thickeners in an amount ranging from 0.01% by weight to 10% by weight and optionally (ii) a curative that catalyzes further condensation of the heat-curable resin at from about 60° C. | 06-02-2011 |
20110171473 | MULTI-LAYERED LIGNOCELLULOSIC MOLDED BODIES WITH LOW FORMALDEHYDE EMISSIONS - A multilayer lignocellulose-containing molding comprising
| 07-14-2011 |
20110217550 | LIGNOCELLULOSE MATERIALS HAVING GOOD MECHANICAL PROPERTIES - A process for the production of a lignocellulose-containing material, in which, based in each case on the lignocellulose-containing material:
| 09-08-2011 |
20110217562 | LIGNOCELLULOSE MATERIALS HAVING GOOD MECHANICAL PROPERTIES - A process for the production of a lignocellulose-containing material, in which, based in each case on the lignocellulose-containing material:
| 09-08-2011 |
20120064355 | MULTI-LAYER LIGNOCELLULOSE-CONTAINING MOLDINGS HAVING LOW FORMALDEHYDE EMISSION - A multilayer lignocellulose-containing molding containing
| 03-15-2012 |
20120138224 | LIGHT LIGNOCELLULOSE MATERIALS HAVING GOOD MECHANICAL PROPERTIES - A process for the production of a light lignocellulose-containing substance having an average density in the range from 200 to 600 kg/m | 06-07-2012 |
20120141772 | LIGHT LIGNOCELLULOSIC MATERIALS HAVING GOOD MECHANICAL PROPERTIES - A process for the production of a light lignocellulose-containing substance having an average density in the range from 200 to 600 kg/m | 06-07-2012 |
20120202041 | MULTILAYER LIGNOCELLULOSE-CONTAINING MOLDINGS HAVING LOW FORMALDEHYDE EMISSION - The invention relates to a multilayer lignocellulose-containing molding. The molding contains a middle layer or a plurality of middle layers containing lignocellulose-containing particles which are obtainable by using a binder and a covering layer or a plurality of covering layers containing lignocellulose-containing particles which are obtainable by using a binder. At least one middle layer contains expanded plastic particles. | 08-09-2012 |
20120219815 | LIGNOCELLULOSE MATERIALS HAVING GOOD MECHANICAL PROPERTIES - A process for the production of a lignocellulose-containing substance having an average density in the range from more than 600 to 900 kg/m | 08-30-2012 |