Rongshi
Rongshi Chen, Liaoning CN
Patent application number | Description | Published |
---|---|---|
20090068053 | HIGH STRENGTH AND HIGH DUCTILITY MAGNESIUM ALLOY AND ITS PREPARATION METHOD - The present invention relates to a high strength and high ductility magnesium alloy and its preparation method. The magnesium alloy in the present invention contains 3˜9 wt % of aluminum, 3.5˜9 wt % of zinc, 0.15˜1 wt % of manganese, 0.01˜2 wt % of antimony, and balanced magnesium. The alloy may further comprise 0˜2 wt. % of one element selected from the group consisting of mischmetal, calcium, and silicon. The room temperature mechanical properties of the T6 heat-treated typical alloy in the present invention are as following: Ultimate Tensile Strength of more than or equal to 270 Mpa, Yield Tensile Strength of more than or equal to 140 Mpa, Elongation of more than or equal to 6%, Brinell hardness of more than or equal to 70, Impact Energy of more than or equal to 12 J. Some of the alloys in the present invention not only possess superior room temperature mechanical properties, but also have very good high temperature mechanical properties. The main alloying elements are easily obtainable and the preparation cost is low enough to meet the demands of large-scale production. The alloy according to the present invention was applicable for most of the casting processes, such as permanent casting, sand casting, die casting, and squeeze casting. | 03-12-2009 |
20140373982 | Magnesium Alloy Sheet with Low Gd Content, High Ductility and the Hot Rolling Technology Thereof - The present invention discloses a magnesium alloy sheet with low Gd content and high ductility and its hot rolling technology, which belongs to the field of metal material technology. The chemical components of the magnesium alloy sheet, based on the mass percent, take up respectively: 0.9˜2.1% as Zn, 0.2˜0.8% as rare earth element, namely Gd, 0˜0.9% as Mn, and the rest as Mg. The magnesium alloy sheet of the present invention is added with relatively lower rare earth element, Gd, which reduces the alloy costs; in addition, magnesium alloy has good rolling performance, which can realize continuous, multi-pass and large-deformation rolling, and also ensure the sheets rolled have non-basal texture and high room-temperature elongation which reaches 35˜50%, wherein the elongation, δ, in the rolling direction is no less than 35% and that in the horizontal direction no less than 45%. | 12-25-2014 |
Rongshi Chen, Shenyang CN
Patent application number | Description | Published |
---|---|---|
20080276681 | Preparation method of laminated composite materials of different alloys - The invention relates to a new preparation technique of composites, in details, i.e. a method of producing laminated composite materials of different alloys. In the preparation method, the bi-layer or multi-layer composites are prepared by means of the equal channel angular extrusion/pressure (ECAE/ECAP). Firstly, the appropriate alloys pairs or groups are selected, and the rational arrangements are carried out after pre-treating surfaces; then, the clad process is performed by extrusion and shear deformation in ECAE die; finally, the composite material is produced after one single pass or multiple passes clad extrusion. The annealing treatment can be performed subsequently to enhance the interfacial bonding strength by diffusion after the clad extrusion, and the heat treatment parameters consist of annealing temperature and holding time, which are chosen carefully to meet the demands of the refining microstructures and good properties for both the interfaces and individual component metals. Consequently, the layer-metal composite is produced with the firmly bonding interface, good microstructures and excellent properties. In the invention, the selection and assembling manners of the materials are very free, such as composites with bi-layer or interval multi-layer manners, and the method is suitable for most of the metal materials. The invention is a new method of fabricating composites and the preparation cost is low enough to meet the demand of large-scale industrial production. | 11-13-2008 |
20110226388 | Chromate-free Conversion Film Solution and the Method of Applying the Solution to Magnesium Alloys - Disclosed herein is a chromate-free conversion film solution and a method of applying the solution to magnesium and magnesium alloys. The solution contains zirconium ions, manganese ions, barium ions and phosphate corrosion inhibitor; and the pH of the said solution is in the range of 1-5; and may further comprise molybdate as accelerant. The method comprises degreasing, acid etching, surface activation, surface adjusting, and film forming steps. The conversion film obtained in accordance with the disclosed method is uniform, smooth, and compact and has high corrosion resistance and good adhesion with paint film. Moreover, the chromate-free conversion film solution is environmentally friendly and possesses fast film growth rates. | 09-22-2011 |
20120288398 | COLD-ROLLING METHOD FOR A WROUGHT MG ALLOY WITH WEAK/NON-BASAL TEXTURE AND A COLD ROLLED SHEET - The present invention relates to a cold-rolling method for cold-rolling a wrought Mg alloy with a weak or non-basal texture as well as a cold-rolled sheet, the method comprising the steps of: pre-treating a billet of the wrought Mg alloy with a weak or non-basal texture, and then cold rolling it; wherein the weak or non-basal texture plane of said billet is selected as a rolling plane, and the rolling direction is parallel to the rolling plane; and said billet is cold rolled at room temperature to a sheet or foil with a thickness of 0.1 to 100 mm, wherein single-pass or multi-pass rolling is used, and the cold rolling is followed by an annealing at 200 to 400° C. for 10 min to 48 h. | 11-15-2012 |
Rongshi Li, Omaha, NE US
Patent application number | Description | Published |
---|---|---|
20140336440 | INHIBITORS OF RHO ASSOCIATED PROTEIN KINASES (ROCK) AND METHODS OF USE - Compounds and compositions having activity as inhibitors of Rho-associated proteinkinases (ROCKs), and methods of making and using the subject compounds are disclosed. | 11-13-2014 |