Patent application number | Description | Published |
20090156748 | Polyolefin Compositions Having Low Gloss - Polyolefin composition comprising, in percent by weight: A) 10-50% of a copolymer of propylene with one or more comonomer(s) selected from ethylene and CH | 06-18-2009 |
20090171018 | Elastoplastic Poyolefin Compositions Having Low Gloss - Elastoplastic polyolefin composition comprising, in percent by weight:
| 07-02-2009 |
20100063207 | POLYOLEFIN COMPOSITIONS HAVING LOW HARDNESS AND LOW GLOSS - A polyolefin composition comprising, in percent by weight: A) 10-25% of a propylene homopolymer or copolymer with up to 8% of comonomer(s); B) 75-90% of a copolymer of ethylene and (i) propylene or (ii) CH | 03-11-2010 |
20100093940 | POLYOLEFIN COMPOSITIONS HAVING LOW HARDNESS AND LOW GLOSS - A polyolefin composition comprising, in percent by weight: A) 20-35% of a propylene homopolymer or copolymer with up to 8% of comonomer(s); B) 65-80% of a copolymer of ethylene and (i) propylene or (ii) CH | 04-15-2010 |
20100119752 | BUTENE-1 TERPOLYMERS AND PROCESS FOR THEIR PREPARATION - Butene-1 terpolymers having
| 05-13-2010 |
20100121011 | 1-BUTENE PROPYLENE COPOLYMER COMPOSITIONS - A 1-butene/propylene copolymer composition having a content of propylene derived units from 1 to 4% by weight, wherein at least 50% of the crystalline polymer is present in the thermodynamically stable, trigonal Form I (detected by DSC analysis) after 100 hours of the first melting at room temperature comprising: b) from 5% by weight to 95% by weight of an atactic 1-butene propylene copolymer having the following features: i) distribution of molecular weight Mw/Mn equal to or lower than 4; ii) no enthalpy of fusion detectable at a differential scanning calorimeter (DSC); and iii) infrared crystallinity lower than 0.5%; b) from 5% by weight to 95% by weight of an isotactic 1-butene propylene copolymer having the following features: isotactic pentads (mmmm) measured by C-NMR, higher than 80%; i) ii) melting point (Tm(II)) higher than 70° C.; and iii) distribution of molecular weight Mw/Mn equal to or lower than 4. | 05-13-2010 |
20100121015 | 1-BUTENE PROPYLENE COPOLYMER COMPOSITIONS - A 1-butene/propylene copolymer composition having a content of propylene derived units from 4 to 10% by weight, wherein at least 50% of the polymer is present in the thermodynamically stable, trigonal form 1 after 100 hours at room temperature, said composition comprising:
| 05-13-2010 |
20100174029 | SOFT POLYOLEFIN COMPOSITIONS WITH IMPROVED PROCESSABILITY - Soft polyolefin composition with improved processability comprising from 8 to 45% by weight of a polypropylene component (A), from 82 to 45% by weight of an elastomeric component (B), and from 10 to 25% by weight of a viscosity reducing agent (C) comprising polybutene-1 and paraffinic wax or grease. The composition is easily processable also by injection moulding and has better tensile properties than compositions in which processability is improved by visbreaking. | 07-08-2010 |
20100222518 | HETEROPHASIC POLYOLEFIN COMPOSITIONS HAVING IMPROVED TENSILE PROPERTIES - Polyolefin composition comprising, in percent by weight: A) 50-75% of a blend of polymers (PP) and (EC | 09-02-2010 |
20130317185 | POLYETHYLENE POLYMERISATION IN GAS PHASE REACTOR - A novel gas phase polymerisation method is devised, for polymerisation of low and ultralow density polyethylene. | 11-28-2013 |