Patent application number | Description | Published |
20100055433 | ATOMIC COMPOSITION CONTROLLED RUTHENIUM ALLOY FILM FORMED BY PLASMA-ENHANCED ATOMIC LAYER DEPOSITION - A metal film composed of multiple atomic layers continuously formed by atomic layer deposition of Ru and Ta or Ti includes at least a top section and a bottom section, wherein an atomic composition of Ru, Ta or Ti, and N varies in a thickness direction of the metal film. The atomic composition of Ru, Ta or Ti, and N in the top section is represented as Ru | 03-04-2010 |
20100092696 | METHOD FOR FORMING METAL FILM BY ALD USING BETA-DIKETONE METAL COMPLEX - A method of forming a single-metal film on a substrate by plasma ALD includes: contacting a surface of a substrate with a β-diketone metal complex in a gas phase; exposing molecule-attached surface to a nitrogen-hydrogen mixed plasma; and repeating the above steps, thereby accumulating atomic layers to form a single-metal film on the substrate. | 04-15-2010 |
20120028469 | METHOD OF TAILORING CONFORMALITY OF Si-CONTAINING FILM - A method of tailoring conformality of a film deposited on a patterned surface includes: (I) depositing a film by PEALD or pulsed PECVD on the patterned surface; (II) etching the film, wherein the etching is conducted in a pulse or pulses, wherein a ratio of an etching rate of the film on a top surface and that of the film on side walls of the patterns is controlled as a function of the etching pulse duration and the number of etching pulses to increase a conformality of the film; and (III) repeating (I) and (II) to satisfy a target film thickness. | 02-02-2012 |
20120058282 | Method of Forming Conformal Film Having Si-N Bonds on High-Aspect Ratio Pattern - A method of forming a conformal dielectric film having Si—N bonds on a substrate having a patterned surface includes: introducing a reactant gas into a reaction space; introducing a silicon precursor in pulses of less than 5-second duration into the reaction space; applying a first RF power to the reaction space during the pulse of the silicon precursor; applying a second RF power to the reaction space during the interval of the silicon precursor pulse, wherein an average intensity of the second RF power during the interval of the silicon precursor pulse is greater than that of the first RF power during the pulse of the silicon precursor; and repeating the cycle to form a conformal dielectric film having Si—N bonds with a desired thickness on the patterned surface of the substrate. | 03-08-2012 |
20130115763 | METHODS FOR FORMING DOPED SILICON OXIDE THIN FILMS - The present disclosure relates to the deposition of dopant films, such as doped silicon oxide films, by atomic layer deposition processes. In some embodiments, a substrate in a reaction space is contacted with pulses of a silicon precursor and a dopant precursor, such that the silicon precursor and dopant precursor adsorb on the substrate surface. Oxygen plasma is used to convert the adsorbed silicon precursor and dopant precursor to doped silicon oxide. | 05-09-2013 |
20150017794 | METHODS FOR FORMING DOPED SILICON OXIDE THIN FILMS - The present disclosure relates to the deposition of dopant films, such as doped silicon oxide films, by atomic layer deposition processes. In some embodiments, a substrate in a reaction space is contacted with pulses of a silicon precursor and a dopant precursor, such that the silicon precursor and dopant precursor adsorb on the substrate surface. Oxygen plasma is used to convert the adsorbed silicon precursor and dopant precursor to doped silicon oxide. | 01-15-2015 |
20150147875 | METHODS FOR FORMING DOPED SILICON OXIDE THIN FILMS - The present disclosure relates to the deposition of dopant films, such as doped silicon oxide films, by atomic layer deposition processes. In some embodiments, a substrate in a reaction space is contacted with pulses of a silicon precursor and a dopant precursor, such that the silicon precursor and dopant precursor adsorb on the substrate surface. Oxygen plasma is used to convert the adsorbed silicon precursor and dopant precursor to doped silicon oxide. | 05-28-2015 |
20150287591 | DEPOSITION OF BORON AND CARBON CONTAINING MATERIALS - Methods of depositing boron and carbon containing films are provided. In some embodiments, methods of depositing B, C films with desirable properties, such as conformality and etch rate, are provided. One or more boron and/or carbon containing precursors can be decomposed on a substrate at a temperature of less than about 400° C. One or more of the boron and carbon containing films can have a thickness of less than about 30 angstroms. Methods of doping a semiconductor substrate are provided. Doping a semiconductor substrate can include depositing a boron and carbon film over the semiconductor substrate by exposing the substrate to a vapor phase boron precursor at a process temperature of about 300° C. to about 450° C., where the boron precursor includes boron, carbon and hydrogen, and annealing the boron and carbon film at a temperature of about 800° C. to about 1200° C. | 10-08-2015 |