Patent application title: Room Temperature Single Phase Li Insertion/Extraction Material for Use in Li-Based Battery
Pierre Gibot (Amiens, FR)
Christian Masquelier (Boves, FR)
Jean Marie Tarascon (Mennecy, FR)
Jean Marie Tarascon (Mennecy, FR)
Stephane Levasseur (Brussels, BE)
Stephane Levasseur (Brussels, BE)
Philippe Carlach (Antwerpen, BE)
IPC8 Class: AH01M4136FI
Class name: Chemistry: electrical current producing apparatus, product, and process current producing cell, elements, subcombinations and compositions for use therewith and adjuncts electrode
Publication date: 2014-04-24
Patent application number: 20140113188
The invention relates to active materials for the manufacture of Li-based
batteries. A crystalline nanometric powdered material with formula
Lix(M, M')PO4, in particular LixFePO4
(0≦x≦1), is disclosed, exhibiting single phase Li
insertion/extraction mechanism at room temperature when used as positive
electrode material in Li-based batteries. Compared to current
LiFePO4, the novel material results in smooth, sloping
charge/discharge voltage curves, greatly simplifying the monitoring of
the state of charge of the batteries. The coexistence of mixed valence
states for Fe (i.e. Fe.sup.IIIVFe.sup.II) is believed to increase the
electronic conductivity in the room temperature single phase
LixFePO4 material, compared to state of the art two-phase
materials. This, together with the nanometric size of the particles and
their sharp monomodal size distribution, contributes to the exceptional
high-rate capability demonstrated in batteries.
1. A Li insertion/extraction powdered material comprising particles of a
crystalline material, the particles having a size distribution d50 of
less than 50 nm, wherein during Li extraction (discharging) from said
material and Li insertion (charging) in said material, the Li
insertion/extraction powdered material remains a single phase material
that is thermodynamically stable at 25.degree. C. for any amount of Li
present in said material.
2. The material of claim 1, wherein d50 is between 10 and 50 nm.
3. The material of claim 1, having a d99 of less than 300 nm.
4. The material of claim 1, having a ratio (d90-d10)/d50 of less than 1.5.
5. A secondary Li-based battery with an electrode comprising the Li insertion/extraction powdered material of claim 1 as an active component wherein during discharging and charging of the active component, the contribution of said electrode to the EMF of the battery at 25.degree. C. varies continuously with the state of charge by more than 0.05 V, for any amount of Li present in said material.
 This application is a national stage application of International
Application No. PCT/EP2008/002195, filed Mar. 19, 2008, which claims
priority to European Patent Application No. 07290328.9, filed Mar. 19,
2007, and U.S. Provisional Patent Application No. 60/907,732, filed Apr.
16, 2007, the entire contents of which is hereby incorporated herein by
 This invention relates to crystalline nanometric materials, in particular to LixFePO4 (0≦x≦1) powder, showing an unusual single phase Li insertion/extraction mechanism at room temperature (25° C.) when used as positive electrode material in Li-based batteries.
 Some years after the original work from Padhi et al. (J. Electrochem. Soc., 144, 1188 (1997)) was published, phospho-olivines LiMPO4 (with M is Fe, Mn, Co . . . ) now appear to be potential candidates as positive electrode materials for rechargeable lithium batteries. Thanks to smart processing, e.g. by carbon coating, Li.sup.+ ions may be extracted out of LiFePO4 leading to room-temperature capacities of about 160 mAh/g, i.e. close to the theoretical capacity of 170 mAh/g. The room-temperature Li insertion/extraction is well known, e.g. from WO2004/001881, to proceed at 3.45 V V5. Li.sup.+/Li, in a two-phase reaction between LiFePO4 and FePO4. Note that, as raised by Striebel et al. (J. Electrochem. Soc., 152, A664 (2005)) while making a compilation of tests of various carbon-coated LiFePO4 compounds, even if the matrix conductivity has been improved by coating, the battery developer would welcome so-far inexistent compounds having a primary particle size in the 50-100 nm range and, overall, attempts should be made to minimise the particle size distribution, in order to yield better power efficiency.
 WO2004/056702 and WO2007/00251 teach techniques to decrease the average particle size down to the 140-150 nm range. Nevertheless, it is admitted by the skilled persons that decreasing the particle size below these values would allow a further increase of the high-power performances.
 Various authors, e.g. Yamada et al. (Electrochem. Solid State Let., 8, A409 (2005)) and in US2007/0031732, have shown that reducing the particle size would allow some deviation from the well described two-phase Li insertion/extraction behaviour. Indeed, materials showing small particle sizes exhibit some limited solid solution (i.e. single phase) domains at room temperature, namely of Li-poor LixFePO4 (x<0.15) and of Li-rich LiyFePO4 (y>0.85). Although it was recognized that the x and y limits, which represent the boundaries of the two-phase domain, may depend upon both the particle size and the particular conditions of the synthesis, materials with a significantly broader single phase domain were never obtained.
 The recent discovery of a complete single phase LixFePO4 (0≦x≦1) solid solution at temperatures of around 350° C. has spurred great interest in assessing its role in the performance of LiFePO4 as cathode material for Li-ion batteries. Nevertheless, whatever the x values, it was clearly demonstrated that the solid solution could not be stabilised at room temperature, thus making it of limited practical interest as standard battery material (Delacourt et al., Nature Mat., 4, 254 (2005); Dodd et al., Electrochem. Solid State Let., 9, A151 (2006)).
 The most obvious distinction between a single phase and a two-phase insertion/extraction mechanism is that the equilibrium potential (EMF) of a single phase system is composition-dependent, while that of a two-phase system is constant over the entire composition range. A single phase electrode will thus show a sloping voltage curve during charge or discharge cycles: this is welcomed by the battery manufacturer as it enables monitoring of the state of charge at reduced cost compared to systems presenting a flat voltage curve.
 Also, it is now admitted that in the two-phase system LiFePO4/FePO4, both end members present very limited electronic conductivity, and that no mixed valence state is present either in FePO4 (Fe.sup.(III)) or in LiFePO4 (Fe.sup.(II)) (Delacourt et al., Electrochem. Soc., 152, A913 (2005). As emphasized by Chiang et al. in US2007/0031732, greater population of both Fe species at every point within the deintercalation range could provide a higher electronic conductivity for the material. A good material conductivity is particularly advantageous with respect to high drain applications.
 The same quest for enhanced material conductivity applies to similar active materials for Li batteries, such as LiMnPO4 and in Li(Fe,M)PO4 (with M is Co and/or Mn), as reported respectively in the patent applications WO2008-77447 and WO2008-77448.
 Further, in US2006/0035150 A1, for the preparation of coated LiFePO4, sources of Li, Fe and phosphate are dissolved in an aqueous solution together with a polycarboxylic acid and a polyhydric alcohol. Upon water evaporation, polyesterification occurs while a mixed precipitate is formed containing Li, Fe and phosphate. The resin-encapsulated mixture is then heat treated at 700° C. in a reducing atmosphere.
 In WO2007/000251 A1, a direct precipitation process is described for preparing crystalline LiFePO4 powder, comprising the steps of:
 providing a water-based mixture having at a pH between 6 and 10, containing a water-miscible boiling point elevation additive, and Li.sup.(I), Fe.sup.(II) and p.sup.(V) as precursor components;
 heating said water-based mixture to a temperature less than or equal to its boiling point at atmospheric pressure, thereby precipitating crystalline LiFePO4 powder.
 An extremely fine 50 to 200 nm particle size is obtained, with a narrow distribution.
 In US2004/0175614 A1, a process is disclosed for the manufacture of LiFePO4, comprising the steps of
 providing an equimolar aqueous solution of Li1+, Fe3+ and PO43-,
 evaporating the water from the solution, thereby producing a solid mixture,
 decomposing the solid mixture at a temperature below 500° C. to form a pure homogeneous Li and Fe phosphate precursor, and
 annealing the precursor at a temperature of less than 800° C. in a reducing atmosphere, thereby forming a LiFePO4 powder.
 The obtained powders have a particle size of less than 1 μm.
 In Delacourt et al., Solid State Ionics 173 (2004) 113-118, the thermodynamics and kinetics governing the precipitation of pure powders of phosphates phases for Li batteries are described. Optimized electrodes were synthesized through a chemical conductive carbon coating at the surface of LiFePO4 prepared by evaporation of an Fe.sup.III-containing aqueous solution.
 The disclosed process is aimed at providing a material with a higher conductivity than that of conventional materials, and at solving the monitoring problem of the state of charge.
 To this end, a powdered Li insertion/extraction material is disclosed, comprising Lix(M,M')PO4 as an active component, wherein 0≦x≦1, M is one or more cations selected from the group consisting of Mn, Fe, Co, Ni, Cu, and M' is an optional substitutional cation selected from the group consisting of Na, Mg, Ca, Ti, Zr, V, Nb, Cr, Zn, B, AI, Ga, Ge, Sn, characterized in that said material is a single phase material that is thermodynamically stable at 25° C. during Li insertion/extraction, for x varying from less than 0.2 to more than 0.8. In the above formula, M is preferably Fe; moreover, an M to M' molar ratio of more than 5, and preferably of more than 8, is advised. When M is Fe and M/M'>5, then the invented material is typically characterized by a crystallographic cell volume lower than 291 Å3, preferably equal to or lower than 290 Å3, and more preferably equal to or lower than 289 Å3. This volume is deduced from XRD measurements using a Pmna or Pmnb space group.
 The invented material is a powder with a preferred particle size distribution with a d50 of less than 50 nm, and preferably between 10 and 50 nm. A d99 of less than 300 nm, and preferably of less than 200 nm is advised. Moreover, a mono-modal particle size distribution where the ratio (d90-d10)/d50 is less than 1.5, preferably less than 1.2, is advised.
 Another aspect of the invention concerns a process for the synthesis of the above-described Lix(M,M')PO4 materials. The process comprises the steps of:
 providing a first water-based mixture having a pH between 6 and 10, containing a bipolar (i.e. water miscible) aprotic additive, and Li and P precursors introduced as Li.sup.(I) and p.sup.(V);
 adding an M precursor as M.sup.(II), and an M' precursor, to said first waterbased mixture, thereby obtaining a second water-based mixture;
 heating said second water-based mixture to a temperature of less than or equal to its boiling point at atmospheric pressure, thereby precipitating the powdered Li insertion/extraction material.
 In a preferred embodiment, Li.sup.(I) is introduced as LiOH.H2O, and p.sup.(V) as H3PO4. It is advisable to adjust the pH of the first mixture by using a proper ratio of LiOH.H2O and H3PO4. The also process covers the synthesis Lix(M,M')PO4, wherein M=Fe, M' being absent, and wherein the pH of the first water-based mixture is between 6.5 and 8, and preferably between 6.5 and 7.5.
 The bipolar aprotic additive is preferably selected and dosed so as to elevate the atmospheric boiling point of the second water-based mixture to between 100 and 150° C., preferably between 105 and 120° C.
 Dimethylsulfoxide is a preferred additive. The first water-based mixture contains between 5 and 50% mol, and preferably between 10 and 30% mol of dimethylsulfoxide.
 In a still preferred embodiment, the precipitating powdered Li insertion/extraction material is subjected to a thermal post-treatment by heating it in non-oxidising conditions, at a temperature of up to 650° C., and preferably of at least 300° C.
 In a still preferred embodiment, an electron conducting substance, or its precursor, is added to either one or more of the first water-based mixture, the second water-based mixture, and the powder before the thermal posttreatment.
 The electronic conducting substance can advantageously be carbon, in particular conductive carbon or carbon fibres, and the precursor of the electron conducting substance can be a carbon-based polymerizable structure.
 Another aspect of the invention concerns a secondary Li-based battery, comprising an anode, an electrolyte and a cathode, said cathode comprising the above-described material.
 Yet another aspect of the invention concerns an electrode mix for secondary Li-based batteries, comprising the above-described material.
 A first embodiment is related to an electrode mix for secondary Li-based batteries with non-aqueous liquid electrolyte, comprising at least 80% wt of the invented material, characterised by a reversible capacity of at least 75% of the theoretical capacity (about 170 mAh/g), when used as an active component in a cathode cycled between 2.5 and 4.5 V vs. Li.sup.+/Li at a discharge rate of 0.1 C at 25° C. The amount of additives (binder and carbon) in the electrode mixture can be limited to less than 20% wt, preferably to less than 10% wt, because the mixture, being pasted on a current collector, needs not to be self-supporting for this type of batteries.
 A second embodiment is related to an electrode mix for secondary Li-based batteries with non-aqueous gel-like polymer electrolyte, comprising at least 80% wt of the invented material, characterised by a reversible capacity of at least 75% of the theoretical capacity when used as an active component in a cathode cycled between 2.5 and 4.5 V vs. Li.sup.+/Li at a discharge rate of 0.1 C at 25° C. The amount of additives in the electrode mixture can be as high as 20% wt in this case, because the mixture, being rolled in the form of a sheet to be laminated to a current collector, needs to be self-supporting during assembly of this type of batteries.
 A third embodiment is related to an electrode mix for secondary Li-based batteries with non-aqueous dry polymer electrolyte, comprising at least 70% wt of the invented material, characterised by a reversible capacity of at least 75% of the theoretical capacity, when used as an active component in a cathode cycled between 2.5 and 4.5 V vs. Li.sup.+/Li at a discharge rate of 0.1 C at 25° C.
 A further embodiment concerns a secondary Li-based battery with an electrode comprising nanometric powdered Lix(M,M')PO4 as an active component, wherein 0≦x≦1, M is one or more cations selected from the group consisting of Mn, Fe, Co, Ni, Cu, and M' is an optional substitutional cation selected from the group consisting of Na, Mg, Ca, Ti, Zr, V, Nb, Cr, Zn, B, AI, Ga, Ge, Sn, characterized in that the contribution of said electrode to the EMF of the battery at 25° C. varies continuously with the state of charge by more than 0.05 V, for x varying from 0.2 to 0.8. In the above formula, M is preferably Fe; moreover, an M to M' molar ratio of more than 5, and preferably of more than 8, is advised. When M is Fe and M/M'>5, then the said nanometric powdered active component is typically characterized by a crystallographic cell volume lower than 291 Å3, preferably equal to or lower than 290 Å3, and more preferably equal to or lower than 289 Å3. This volume is deduced from XRD measurements using a Pnma or Pmnb space group.
 By "continuously varying EMF" is meant a continuously sloping charge/discharge voltage curve. This slope, according to the present invention, amounts to at least 5 mV per inserted/extracted Li, and preferably to at least 15 mV per inserted/extracted Li, and this along the complete charge/discharge cycle.
 The said nanometric powdered active component has a preferred particle size distribution with a d50 of less than 50 nm, and preferably between 10 and 50 nm. A d99 of less than 300 nm, and preferably of less than 200 nm is advised. Moreover, a mono-modal particle size distribution where the ratio (d90-d10)/d50 is less than 1.5, preferably less than 1.2 is advised.
 It should be noted that, in the invented material, M and M' are considered as at least partially interchangeable, whilst however respecting electroneutrality rules assuming Li.sup.(I), M.sup.(II), M'.sup.(I) to (V), and p.sup.(V).
 Products finer than 10 nm are not particularly advisable, as they could lead to processability problems during electrode manufacturing.
 According to the invented process, the first water-based mixture has a pH between 6 and 10, preferably 6 to 8, in order to avoid precipitation of Li3PO4 as impurities.
 Use is made of a bipolar additive as a co-solvent that will increase the precipitate nucleation kinetics, and thus reducing the size of the room temperature single phase Li insertion/extraction LixFePO4 (0≦x≦1) nanometric particles. In addition to being bipolar, i.e. miscible with water, useful co-solvents should be aprotic, i.e. show only a minor or complete absence of dissociation accompanied by release of hydrogen ions. Cosolvents showing complexation or chelating properties such as ethylene glycol do not appear suitable as they will reduce the kinetics of precipitation of LixMPO4 and thus lead to larger particle sizes. Suitable dipolar aprotic solvents are dioxane, tetrahydrofuran, N-(C1-C18-alkyl) pyrrolidone, ethylene glycol dimethyl ether, C1-C4-alkylesters of aliphatic C1-C6-carboxylic acids, C1-C6-dialkyl ethers, N,N-di-(C1-C4-alkyl)amides of aliphatic C1-C4-carboxylic acids, sulfolane, 1,3-di-(C1-C8alkyl)-2-imidazolidinone, N-(C1-C8-alkyl)caprolactam, N,N,N',N'-tetra-(C1-C8-alkyl)urea, 1,3-di-(C1-C8-alkyl)-3,4,5,6-tetrahydro-2(1H)-pyrimidone, N,N,N',N'-tetra-(C1-C8-alkyl)sulfamide, 4-formylmorpholine, 1formylpiperidine or 1-formylpyrrolidine, in particular N-(C1-C18-alkyl)pyrrolidone, N,N-di-(C1-C4-alkyl)amid-e of aliphatic C1-C4-carboxylic acids, 4-formylmorpholine, 1-formylpiperidine or 1-formylpyrrolidine, preferably N-methyJpyrrolidone (NMP), N-octylpyrrolidone, Ndodecylpyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide, 4-formylmorpholine, 1-formylpiperidine or 1-formylpyrrolidine, particularly preferably N-methylpyrrolidone, N,N-dimethylformamide, N,Ndimethylacetamide or hexamethylphosphoramide. Other alternatives such as tetraalkyl ureas are also possible. Mixtures of the abovementioned dipolar aprotic solvents may also be used. In a preferred embodiment, dimethylsulfoxide (DM50) is used as solvent.
 It cannot be excluded that the novel room temperature single phase insertion/extraction material could lead to a two-phase system at temperatures well below 25° C., such as below 10° C. This phase transition should however be reversible. Its effect should therefore only minimally affect the operation of batteries in most practical circumstances.
 The disclosed process leads to an initial material that may contain traces of Fe(III). Due to the nanometric particle size, some Fe.sup.(III) could arise from a deviation from stoichiometry at the surface of the material. The presence of Fe.sup.(III) could also be due to a second amorphous phase, most likely LiFePO4(OH) or FePO4.nH2O, at the surface of the crystals or at grain boundaries. The skilled person may minimize the Fe.sup.(III) by working under reducing atmosphere or by relying on reducing agents such as hydrazine or SO2. The possible Li deficit in the initial material could moreover be compensated during the first full discharge cycle of the battery if the environment is able to provide the necessary Li (as it is likely the case in many practical batteries).
 Compared to state of the art LiFePO4 materials, the advantages of the invented material are:
 a sloping charge/discharge curve, allowing direct monitoring of the state of charge by simple potential measurement;
 a nanometric particles size, which alleviates kinetic limitations due to Li ion transport within the particles, and allows fast charge/discharge of the battery;
 a narrow particle size distribution, ensuring a homogeneous current distribution within the battery; this is again especially important at high charge/discharge rates, where finer particles would get more depleted than coarser ones, a phenomenon leading to the eventual deterioration of the particles and to the fading of the battery capacity upon use; a narrow particle size distribution furthermore facilitates the manufacture of electrodes;
 the coexistence of mixed valence state for Fe (i.e. Fe.sup.(III)/Fe.sup.(II)), which is believed to increase the electronic conductivity of the room temperature single phase LixFePO4 material compared to state of the art two-phase materials, represented as (1-x)FePO4+xLiFePO4 (0≦x≦1).
SUMMARY OF THE FIGURES
 FIG. 1: Galvanostatic charge/discharge curve of the invented material at 25° C. and C/20 rate, showing a sloping voltage curve. The plot shows the voltage of the battery as a function of the normalized capacity; 0% state of charge (SOC) corresponds to starting LiFePO4 material, while 100% corresponds to charged delithiated FePO4 material.
 FIG. 2: FEG-SEM picture of product of the Example, showing the small particle size and the sharp particle size distribution.
 FIG. 3: Volumetric particle size distribution and cumulative distribution (% vs. nm) for the product of the Example showing d50 values about 45 nm, while the relative span, defined as (d90-d10)/d50, is about 1.2 (d10=25 nm, d90=79 nm).
 FIG. 4: In situ XRD recorded at different states of charge and at 25° C. for invented material; 0% state of charge (SOC) corresponds to starting LiFePO4 material, while 100% corresponds to charged delithiated FePO4 material.
 FIG. 5: Evolution with composition of the cell parameters for LixFePO4 (0≦x≦1) calculated from the in situ XRD recorded at measured at 25° C. at different states of charge. This clearly shows a continuous solid solution between LiFePO4 and FePO4 with continuous variation between the limiting values of the cell parameters as the lithium concentration varies from 1 to 0.
 FIG. 6: Galvanostatic charge/discharge curve of state of the art material at 25° C. and C/20 rate, showing the constant voltage curve. The plot shows the voltage of the battery as a function of the normalized capacity; 0% state of charge (SOC) corresponds to starting LiFePO4 material, while 100% corresponds to charged delithiated FePO4 material.
 FIG. 7: in situ XRD recorded at different states of charge for state of the art products; 0% state of charge (SOC) corresponds to starting LiFePO4 material, while 100% corresponds to charged delithiated FePO4 material.
 FIG. 8: Evolution with composition of the cell parameters for (1-x)FePO4+xLiFePO4 (0≦x≦1) calculated from the in situ XRD recorded at different states of charge. This clearly shows a classical two-phase system, the proportion of each end member varying with the lithium concentration in the material.
 The invention is further illustrated in the following example. In a first step, DMSO is added to a solution of 0.1 M H3PO4, diluted in H2O under stirring. The amount of DMSO is adjusted in order to reach a global composition of 50% vol. water and 50% vol. DMSO.
 In a second step, an aqueous solution of 0.3M LioH.H2O is added at 25° C. in a quantity so as to increase the pH up to a value between 6.5 and 7.5, and leading to the precipitation of Li3PO4.
 In a third step, a solution of 0.1M Fe(II) in FeSO4.7H2O is added at 25° C. This is believed to lead to the re-dissolution of Li3PO4. The final Li:Fe:P ratio in the solution is close to 3:1:1. By adding the Fe(II) precursor after the pH of the solution has been set at a certain value between 6.5 and 7.5, it is possible to perform a controlled precipitation of Fe-species resulting in much lower particle sizes than obtained in the prior art.
 In a fourth step, the temperature of the solution is increased up to the solvent boiling point, which is 108 to 110° C. After 6 h, the obtained precipitate is filtered and washed thoroughly with water.
 The powdery precipitate is pure crystalline LiFePO4, according to XRD measurements. The full pattern matching refinement done on XRD pattern (Pmnb space group) leads to cell parameters a=10.294 Å3, b=5.964 Å3 and c=4.703 Å3, corresponding to a crystallographic cell volume of 288.7 Å3. The FEG-SEM picture on FIG. 2 shows monodisperse small crystalline particles in the 30 to 60 nm range. The volumetric particle size distribution of the product was measured by using image analysis. As shown in FIG. 3, the d50 values is about 45 nm, while the relative span, defined as (d90d10)/d50, is about 1.2 (d10=25 nm, d90=79 nm).
 A slurry is prepared by mixing the LiFePO4 powder obtained with the process described above with 10% wt carbon black and 10% wt PVDF into N-Methyl Pyrrolidone (NMP) and deposited on an AI foil as current collector. The obtained electrode containing 80% wt active material is used to manufacture coin cells, using a loading of 6 mg/cm2 active material. The negative electrodes are made of metallic Li. The coin cells are cycled in LiBF4 based electrolyte between 2.5 and 4.0 V. FIG. 1 shows that high reversible capacity is obtained at low rate with a sloping voltage curve upon cycling characteristic of a single phase Li insertion/extraction mechanism. It should be emphasised that the curve of FIG. 1 has been recorded in galvanostatic conditions, and, as such, only approximates the EMF of the electrode. The EMF is in this case varying continuously as a function of Li insertion/extraction; the slope of the EMF curve is thus definitely nonzero, although it might be slightly less pronounced than in the figure.
 FIG. 4 shows in situ XRD data collected in the battery upon cycling. It is clearly visible on FIG. 5 that the insertion/extraction proceeds from LiFePO4 to FePO4 with a continuous evolution of the cell parameters, which evidences the presence of a single LixFePO4 (0≦x≦1) phase. It also emphasizes the good reversibility of this single phase mechanism upon cycling.
 As a counter example, materials are synthesised according to the example illustrating WO2007/000251. Compared to the example according to the invention, one notes that the order of addition of the reactants is different; this change is of crucial importance with respect to the final particle size of the precipitated material, this latter being about 130 to 150 nm for product precipitated according to the mentioned prior art. It is understood that the difference between the present invention and this prior art lies in the fact that the Fe-precursor is added to a solution having already a fixed and stable pH, between 6.5 and 7.5; whilst in the prior art the Fe-precursor is added to a solution having a pH of less than 6, whereafter the addition of the Li-precursor raised the pH to around 7. The Fe-precursor can also be added in a solid form.
 Also, the obtained counter example material, as characterized by Rietveld refinement from XRD pattern, shows a crystallographic cell volume of 291.7 Å3.
 With his material, batteries are prepared as described above. FIG. 6 shows the charge/discharge curve of the prior art material at room temperature and C/20 cycling rate. There is a constant voltage plateau, which is characteristic of a two-phase Li insertion/extraction mechanism. It should be emphasised that the curve of FIG. 6 has been recorded in galvanostatic conditions, and, as such, only approximates the EMF of the cell. The EMF is in this case constant, the slope of the EMF as a function of Li insertion/extraction being essentially zero.
 FIG. 7 shows in situ XRD recorded at different state of charge/discharge. The evolution of the cell parameters is illustrated in FIG. 8. This clearly shows a classical two-phase system, the proportion of each end member FePO4 and LiFePO4 varying with the lithium concentration in the material, as opposed to the product according to the invention.
Patent applications by Christian Masquelier, Boves FR
Patent applications by Jean Marie Tarascon, Mennecy FR
Patent applications by Philippe Carlach, Antwerpen BE
Patent applications by Pierre Gibot, Amiens FR
Patent applications by Stephane Levasseur, Brussels BE